Zinc borate
Molecular formula: 2ZnO•3B2O3•3.5H2O Molecular weight: 434.5
1. Technical indicators
|
Product Name |
Zinc Borate |
Grade |
Industrial Grade |
|
Product Model |
ZB2335 |
Primary Product Use |
Flame Retardant/Smoke Suppressant |
|
Technical Index |
Standard Value |
||
|
Appearance |
White Powder |
||
|
Whiteness % |
≥95.0 |
||
|
Zinc Oxide (ZnO) % |
36.5~39.5 |
||
|
Boron Oxide B2O3 % |
46.0~48.0 |
||
|
Loss On Ignition % |
13.0~14.5 |
||
|
Surface Water % |
≤0.6 |
||
|
Particle Size D50 μm |
4~6 |
||
|
Fineness (Residue on 45μm Sieve) |
≤0.02 |
||
2. RECOMMEND APPLICATION:
THE MAIN APPLICATIONS INCLUDE FLEXIBLE PVC (WIRE AND CABLE MATERIALS, CONVEYOR BELTING, WALL CONVER, FLOOR TILES), RIGID PVC (PANELS), THEMOSET POLYESTER (PANELS), SILICONES (INSULATOR, COATINGS AND WIRE INSULATIONS) AND EPS (SPHERICAL PARTICLES AND PANELS).
ZINC BORATE, ARE USED AS FIRE RETARDANT AND SMOKE SUPPRESSANT ADDITIVES IN POLYMERS, PLASTICS, AND RUBBER APPLICATIONS.
- WIRE AND CABLE MATERIALS
- WALL COVERINGS
- FLOORING PRODUCTS
- CONVEYOR BELTS
- ROOFING MEMBRANES
- SKYLIGHT PANELS
PRESERVATIVE FOR BIO-COMPOSITES: ZINC BORATE IS USED TO LEND DURABILITY TO THESE PRODUCTS, INCLUDING ORIENTED STRAND BOARD (OSB), LAMINATED STRAND LUMBER, ORIENTED STRUCTURAL STRAW BOARD, PARTICLE BOARD, ENGINEERED BAMBOO SCRIMBER, WAFERBOARD, AND WOOD-PLASTIC COMPOSITES
3. PACKAGING & STORAGE:
25 KG/BAG, PALLETIZED, 18 MT/20’GP
500 KG/BAG, PALLETIZED, 10MT/20’GP
500 KG/BAG, PALLETIZED, 20MT/40’GP
THE PRODUCT SHOULD BE STORED UNDER DRY AND CLEAN CONDITIONS IN ITS
ORIGINAL PACKING.THE MOISTURE MAY INCREASE IF NOT UNDER DRY CONDITION.
GUARANTEED FOR 12 MONTHS FROM PRODUCTION DATE WHEN STORED UNDER ABOVE STORAGE CONDITIONS.
POPULAR PRODUCTS
-
Antimony TrioxideAntimony trioxide (also referred to as antimony oxide, commonly known as antimony white)Antimony Trioxide0.00Antimony trioxide (also referred to as antimony oxide, commonly known as antimony white) -
TRIS(2-CHLOROETHYL) PHOSPHATE (TCEP)Because there are both chlorine atoms and phosphate groups in the molecule, this product has significant flame retardant and plasticizing properties for plastics, unsaturated resins, glass fiber reinforced plastics, and rubber products.TRIS(2-CHLOROETHYL) PHOSPHATE (TCEP)0.00Because there are both chlorine atoms and phosphate groups in the molecule, this product has significant flame retardant and plasticizing properties for plastics, unsaturated resins, glass fiber reinforced plastics, and rubber products. -
TRIS(2-CHLOROPROPYL) PHOSPHATE (TCPP)P erform ance and A pplication This product is colorless to pale yellow oily liquid, soluble in benzene, alcohol, ester and carbon tetrachloride. A t 20 ℃ , its aquatic solubility is 1.6g/L. This product is insoluble in aliphatic hydrocarbons. C hlorine content is 32.5% , and phosphorus content is 9.5% . A s the m olecule contains both phosphorus and chlorine, its flam e-retardant properties are very significant; at the sam e tim e, the product is plasticized, m oisture-proof, anti-static and so on. Therefore, it is an additional flam e retardant. This product is suitable for flam e retardancy of polyurethane, P V C , polystyrene, phenolic resin, acrylic resin, rubber and coating. It is generally used w ith antim ony oxide to increase the flam e-retardant efficiency of antim ony oxide. The am ount is about 10%TRIS(2-CHLOROPROPYL) PHOSPHATE (TCPP)0.00P erform ance and A pplication This product is colorless to pale yellow oily liquid, soluble in benzene, alcohol, ester and carbon tetrachloride. A t 20 ℃ , its aquatic solubility is 1.6g/L. This product is insoluble in aliphatic hydrocarbons. C hlorine content is 32.5% , and phosphorus content is 9.5% . A s the m olecule contains both phosphorus and chlorine, its flam e-retardant properties are very significant; at the sam e tim e, the product is plasticized, m oisture-proof, anti-static and so on. Therefore, it is an additional flam e retardant. This product is suitable for flam e retardancy of polyurethane, P V C , polystyrene, phenolic resin, acrylic resin, rubber and coating. It is generally used w ith antim ony oxide to increase the flam e-retardant efficiency of antim ony oxide. The am ount is about 10% -
Zinc borateZinc borate is an inorganic additive flame retardant, which is characterized by good thermal stability, both flame retardant and smoke suppression. It can replace antimony trioxide in some products and can also be used in conjunction with other inorganic flame retardants.Zinc borate0.00Zinc borate is an inorganic additive flame retardant, which is characterized by good thermal stability, both flame retardant and smoke suppression. It can replace antimony trioxide in some products and can also be used in conjunction with other inorganic flame retardants. -
Aluminum hydroxideAluminum Hydroxide (also known as: hydrated alumina, abbreviated as: ATH) Molecular formula: AL(OH)3 or AL2·3H2O Molecular weight: 78Aluminum hydroxide0.00Aluminum Hydroxide (also known as: hydrated alumina, abbreviated as: ATH) Molecular formula: AL(OH)3 or AL2·3H2O Molecular weight: 78 -
magnesium hydroxidePhysical properties: Magnesium hydroxide mainly has three specifications of 325 mesh, 1250 mesh, 2500 mesh, and 5000 mesh. Remarks: Surface modification treatment can be carried out according to customer requirements. Special instructions are required when ordering.magnesium hydroxide0.00Physical properties: Magnesium hydroxide mainly has three specifications of 325 mesh, 1250 mesh, 2500 mesh, and 5000 mesh. Remarks: Surface modification treatment can be carried out according to customer requirements. Special instructions are required when ordering.
CONTACT US
Address: South of East Extension, Chuangxin Street, High-tech Development Zone, Yucheng City, Shandong Province
Wechat QR code
Copyright : Shandong Chenxu New Material Co., Ltd. 鲁ICP备09047114号 鲁公网安备 37148202000364号 Powerby : 300.cn jinan